E-600 HIGH LUSTER STEEL FINISH COAT IS A TWO COMPONENT TOP COAT

PRODUCT INFORMATION:

E-600 STEEL OVERCOAT SYSTEM

After E-600 Overcoat System

After E-600 Overcoat System

During Application Of E-600 Over E-400
Red River Gorge

After E-600 ENVIROSHIELD
After E-600
Red River Gorge

Small Amount Of Power Tool Cleaning Necessary For Flash Rust After Water Jetting At 36,000 P.S.I. Before E-400- E-401 and E-600 Finish Coat Is

Power Wash Chilling Tank

E-600 Finish Coat Over E-400 Primer

ENVIROSHIELD 600 FINISH COAT IS A TWO COMPONENT TOP COAT.

E-600 Independent Test Results

FINISH: HIGH LUSTER.
COLOR: CUSTOM COLORS AVAILABLE.

USES:

E-600 FINISH COAT IS AN EXTRAORDINARY HIGH STRENGTH, HIGH GLOSS LONG LASTING TOP COAT.
ENVIROSHIELD 600 IS HIGHLY RESISTANT TO CHEMICAL CONTACT, WET WEATHER CONDITIONS, ABRASION, CORROSIVE FUMES, AND UVRS. ENVIROSHIELD 600 IS EXCELLENT FOR TOP COATING USE ENVIROSHIELD 400 PRIMER AS A SEALER AND ENVIROSHIELD 500 MID COAT WHEN A MID COAT MAY BE SPECIFIED.

E-600 FINISH COAT IS AN EXCELLENT TOP COAT FOR PRIMERS AND MID COATS FUR STRUCTURAL STEEL SUCK AS BRIDGES, TANKS, AND TOWERS. U.S.D.A. APPROVED FOR FOOD ESTABLISHMENTS.

SURFACE PREPARATION:

SURFACES MUST BE FREE FROM ALL MOISTURE, DIRT, OIL, GREASE AND ALL OTHER CONTAMINANTS. WATER BLASTING IS RECOMMENDED.

PRODUCT DESCRIPTION:

ENVIROSHIELD 600 IS A TWO COMPONENT, TWO PACKAGE COATING-PRODUCTS [A] AND [B].
PRODUCT [A] CONTAINS HYDROXYL POLYACRYLATE RESIN
PRODUCT [B] CONTAINS CURING AGENT ALIPHATIC POLYISOCYANATE RESIN BASED ON HEXAMETHYLENE DIISOCYANATE.

MIXING:

VOLUMETRIC MIX IS 5.66-TO 1 BASE CONVERTER.
STIR WELL PART (A) BEFORE ADDING PART [B]
WHILE STIRRING, ADD PART [B] AND CONTINUE TO STIR WELL.
KEEP UNUSED PRODUCT COVERED SINCE PART [B] REACTS TO MOISTURE.

THINNING: NOT RECOMMENDED

POT LIFE:

1 HR. ® 100 DEGREES F. AND ® 90 % R. HUMIDITY, USABLE.
2 HRS. ® 78 DEGREES F AND ® 50% R. HUMIDITY, USABLE.
3 HRS. ® 78 DEGREES F AND ® 48 % R. HUMIDITY, USABLE.

PRODUCT TECHNICAL DATA:

WEIGHT PER GAL: 11.57 +- 0.23 LBS.
WEIGHT SOLIDS: 7 5 % + ? 1. 5 0 %
VOLUME SOLIDS: 6 1. 6 7 % + ? 1. 5 %
VOC: 333 GRAMS PER LITER OR 2.78 LBS. PER GAL.
VOC COMPOUNDS: 225-230 (UN THINNED)
STORAGE LIFE: ONE [1) YEAR.
VISCOSITY: STORMIER MTR. ASTM D 562-85 INITIAL 73 KU AFTER 1 HR. 80 KU -AFTER 5 HRS. 94 KU

Before Overcoating With E-Systems
JFK Bridge

E-600 Independent Test Results

CURING TIME:

TO TOUCH :            3 1/2 HRS.
TO HANDLE :           5-6 HRS.
TO RECOAT :           8 HRS. @ 25 C. @ 50 % HUM
TO HARD DRY :         16 1/2 HRS
TO MAR-FREE:          25 HRS. C.

APPLICATION:

SAG RESISTANCE	RECOMMENDED FILM THICKNESS
LENATA DRAWDOWN	2.5-4.0 MILS DRY 3.5-5.5 WET

NO SAG ® 1.0 MIL	1.0 MIL D.F.T. 946 SQ. FT. PER GAL.
NO SAG 0 2.5 MILS	1.5 MIL D.F.T. 630 SQ. FT. PER GAL.
NO SAG 0 3.4 MILS	2.0 MIL D.F.T. 473 SQ. FT. PER GAL.
NO SAG 0 4.25 MILS	2.5 MIL D.F.T. 378 SQ. FT. PER GAL.
NO SAG 0 5.0 MILS	3.0 MIL D.F.T. 315 SQ. FT. PER GAL.
SAG 0 6.0 MILS	3.5 MIL D.F.T. 270 SQ. FT. PER GAL.
SAG 0 6.75 MILS	4.0 MIL D.F.T. 235 SQ. FT. PER GAL.
SAG 0 7.0 MILS	4.5 MIL D.F.T. 210 SQ. FT. PER GAL.
SAG 0 7.75 MILS	5.0 MIL D.F.T. 190 SQ. FT. PER GAL.

CAUTION:

SURFACE TEMPERATURE MUST BE AT LEAST FIVE (5) DEGREES F. ABOVE DEW POINT BEFORE APPLICATION. DO NOT APPLY UNDER 40 D. F. OR OVER 95 D. F.

SAFETY PROCEDURES:

SEE MSDS Sheet : Part 1, Part 2

EQUIPMENT:

APPLY WITH BRUSH, SPRAY OR ROLLER AIRLESS SPRAYER USE TIP SIZE 0.009 OR 0.013

CLEANUP:

USE MEK OR A BLEND OF MEK 0 20%, PM ACETATE 0 30 % AND AROMATIC 100 0 50 % FOR