E-400 Moisture Cure Rescue
Project
I-75 Rockcastle County
During The
E-400 Moisture Cure Rescue Project
I-75 Rockcastle County
Final Inspection after
E-400 Primer and E-600 finish Coat
Green River Bridge
Before Cleaning
Cumberland County
Small Amount Of Power
Tool Cleaning Necessary For Flash Rust After Water Jetting
At 36,000 P.S.I. Before E-400- E-401 and E-600 Finish Coat
Is
Power Wash Chilling Tank
E-600
Finish Coat Over E-400 Primer
Before Overcoating With
E-Systems
JFK Bridge
Before E-400 And E-600
Red River Forge
After E-400 And E-600
Clark County |
A
MOISTURE CURE POLYURETHANE NON-LEAFING ALUMINUM PRIMER
STEEL OVERCOAT SYSTEMS E-400 IS AN ECONOMICAL, ONE COMPONENT, ENVIRONMENT
FRIENDLY MOISTURE CURE PRIMER OF HIGH SOLID NON-LEAFING
ALUMINUM.
COLOR: SILVER
FINISH: FLAT
CHEMICAL FAMILY:
POLY ISOCYANATE - PREPOLYMER
USES:
- STEEL OVERCOAT SYSTEMS E-400
IS EXCELLENT FOR OVERCOATING
- STRUCTURAL STEEL AND OTHER METAL SURFACES
WHEN LITTLE PREPARATION IS DESIRED
TO ACCOMMODATE FIRST STAGE ENCAPSULATION OF RUST,CORROSION
AND OLD LEAD PAINT.
- STEEL OVERCOAT SYSTEMS E-400
ELIMINATES THE NEED FOR SAND BLASTING WHEN 4000+ P.S.I.
WATER BLASTING AND A REASONABLE AMOUNT OF POWER AND
HAND TOOL CLEANING IS DONE.
- STEEL OVERCOAT SYSTEMS
E-400'S ABILITY TO ENCAPSULATE OLD PAINT AND RUST IS
ENHANCED WHEN A SECOND COAT IS USED
BEFORE TOP COATING.
- STEEL
OVERCOAT SYSTEMS E-400 MUST BE TOP COATED
IN EVERY INSTANCE, DUE TO PRIMERS LACK OF LIGHT STABILIZERS.
- STEEL OVERCOAT SYSTEMS E-400
AFFORDS HIGH RESISTANCE TO CORROSION, MOISTURE, CHEMICALS,
ABRASION AND UNDERCUTTING.
SURFACE PREPARATION:
SURFACES MUST BE FREE FROM ALL MOISTURE, DIRT, OIL, GREASE
AND OTHER CONTAMINANTS. FOR BEST RESULTS, POWER WASH AND
TOOL CLEAN, THEN BRUSH FIRST COAT OVER SUBSTRATE BEFORE
APPLYING SECOND COAT WITH BRUSH, ROLLER OR SPRAY.
PRODUCT TECHNICAL DATA:
| WEIGHT SOLIDS: |
69.0 +. 2.0 %. |
| WEIGHT PER GAL: |
9.6 LBS. PER
GAL.+-O.2 LBS. PER GAL. |
| VOLUME SOLIDS: |
59.19 % +- 1.5
% |
| VOC LBS. PER GAL: |
2.71 LBS. |
| GRAMS PERIL |
322.1 |
| RECOMMENDED
D.F.T.: 2 - 3 MILS DRY. |
|
|
| CURING
TIME: |
|
|
TO TOUCH
3 HRS. |
|
TO HANDLE
3-4 HRS. |
|
TO RECOAT
4 HRS. 0 77 F. @ 50% R. HUMIDITY. |
|
TO RECOAT
IN BELOW NORMAL TEMP- 24 HRS. |
|
|
| STORAGE
LIFE: |
ONE YEAR
@ 77 F. ( 25 C ) |
APPLICATION PROCEDURES:
PREPARE PRODUCT BY THOROUGHLY STIRRING, MAKING SURE NO
PIGMENTS STAY ON BOTTOM.
KEEP PRODUCT CONTAINER CLOSED WHEN NOT USING, SINCE PRODUCT
REACTS TO MOISTURE.
DO NOT THIN, SINCE VISCOSITY WILL REMAIN CONSTANT WHEN
CONTAINER STAYS CLOSED.
APPLY WITH BRUSH, SPRAY OR ROLLER.
AIRLESS SPRAY:
USE TIP SIZE 0.017 OR 0.013. HOSE SIZE: 114 TO 318
INCH. FILTER: USE 60 MESH.
RECOAT TIME:
FOR COLD WEATHER APPLICATION, A LONGER DRYING TIME IS RECOMMENDED,
A MINIMUM OF NO LESS THAN 24 HRS.
FOR WARM TO HOT WEATHER RECOAT TIME MAY BE SHORTENED TO
AS LITTLE AS 4 HRS.
MUST BE RECOATED WITHIN 5 DAYS.
SURFACE TEMPERATURE MUST BE AT LEAST FIVE [5} DEGREES ABOVE
DEW POINT BEFORE APPLICATION.
FOR ADDITIONAL INFORMATION,
CONTACT US.
COVERAGE
RATES:
SPRAY, BRUSH OR ROLLER: |
|
WET MILLS 3.5 = 2.5 MILS DFT=APPROX:
425 SQ. FT. PER GALLON
|
WET MILLS 4.5=3.0 MILS DFT=
APPROX: 360 SQ. FT. PER GALLON
|
| |
| FOR
HIGH BUILD-SPRAY ONLY: |
| WET
MILLS 7.5 = 5.0 MILS DFT = APPROX: 225 SQ. FT. PER
GALLON |
| WET
MILLS 6.0 4.0 MILS DFT = APPROX: 275 SQ. FT. PER
GALLON |
| WET
MILLS 4.5 = 3.0 MILS DFT = APPROX: 375 SQ. FT. PER
GALLON |
|
|
| SAG
RESISTANCE: |
| NO
SAG ON LENATA DRAWDOWN SCALE THROUGH 6 WET MILS. |
| 1/32"
DRAG @ 8 MILS WET. |
CLEANUP: USE (XYOL)
XYLENE TO FLUSH AND CLEAN IMMEDIATELY AFTER EQUIPMENT USE.
DO NOT ALLOW MOISTURE OR ALCOHOL NEARPRODUCT OR EQUIPMENT.
SAFETY PROCEDURES:
SEE MSDS Sheet |