Water blasting before
E-2000 Primer - Sealer
During Application E-2000
Clear Primer - Sealer
During Application of
E-600 Over E-2000 Sealer
E-600
Finished Product
3.5 year Test Of E-2000
Primer - Sealer and E-600 Finish Coat
|
E - 2000: IS AN ECONOMICAL
ONE COMPONENT COATING.
COLOR: CLEAR, RED OXIDE
AND OTHER COLORS ARE AVAILABLE.
CHEMICAL RELATION:
POLY ISOCYANATE - PREPOLYMER.
USES:
E - 2000 IS AN EXCELLENT PRIMER-SEALER, USED ON
SUBSTRATES AS,
- ASBESTOS
- CONCRETE
- BRICK
- STEEL
- WOOD
M.LO. AND OTHER PIGMENTS ARE USED FOR PENETRATING PRIMER-
SEALERS, FOR STEEL STRUCTURES, SUCH AS BRIDGES, TANKS AND
WHERE A FIRST STAGE SEALER IS DESIRED UNDER BARRIER COATS
AND FINISH COATS.
E - 2000 SHOULD
BE TOP COATED SOON AFTER DRYING.
E - 2000 AFFORDS HIGH RESISTANCE TO CORROSION, MOISTURE,
CHEMICAL, ABRASION AND UNDERCUTTING.
E - 2000 IS APPROVED FOR FOOD PLANTS.
| WEIGHT
SOLIDS: |
%69.O
+- 2% |
| WEIGHT
PER GAL: |
9.6
LBS. |
| VOLUME
SOLIDS: |
%
60.0 |
| VOC
LBS. PER GAL.: |
3.33
GRAMS |
| PERIL |
395.8 |
|
|
| RECOMMENDED
D.F.T. @ 2-4 MILS |
CURING
TIME TO TOUCH: |
2 HRS. |
TO HANDLE:
|
3-4 HRS. |
TO RECOAT
@ 77 DEGREES F. @ 50% HUMIDITY: |
4 HRS. |
COVERAGE RATES: [ THEORETICAL
]
| 5.5
D.F.T. |
=145
SQ. FT. PER GAL. |
|
4.0 |
=175 |
|
3.5 |
=275 |
|
3.0 |
=315 |
|
2.5 |
= 375 |
|
2.0 |
=
475 |
|
1.0 |
=946 |
SURFACE PREPARATION:
SURFACE MUST BE FREE OF ALL MOISTURE, DIRT, OIL, GREASE
AND OTHER CONTAMINANTS.
TOOL CLEANING:
LITTLE HAND TOOL CLEANING IS NECESSARY WHEN HIGH PRESSURE
WATER BLASTING IS USED.
RECOAT TIME:
TOP COAT SHOULD BE APPLIED IN LESS THAN 2 DAYS.
APPLICATION:
STIR THOROUGHLY, MAKING SURE PRODUCT IS ONE CONSISTENCY.
KEEP CONTAINER CLOSED WHEN NOT IN USE, AS PRODUCT REACTS
WITH ATMOSPHERIC MOISTURE
EQUIPMENT:
APPLY WITH ROLLER, SPRAY OR BRUSH.
SPRAY TIP SIZE: 0.013 to 0.017
HOSE SIZE: 114 TO 3/8 INCH.
CAUTION: SURFACE Temperature
MUST BE [5] DEGREES ABOVE THE DEWPOINT BEFORE APPLYING.
CLEANUP: USE XYLENE
TO FLUSH AND CLEAN EQUIPMENT IMMEDIATELY AFTER USE.
SAFETY PROCEDURES:
SEE MSDS Sheet :(click here)
|